Ultra-micro latent PM2100 accelerator is a urea-modified product, which is perfectly compatible with epoxy resin. Epoxy resin one-component adhesives, sealing materials, potting materials and various powder coatings prepared with this accelerator are featured with the small dosage (2-5% of the resin), non-curing at the room temperature, over half year storage life at the room temperature (25 °C), quick curing (within 30 min) at 120-130 ℃. The detailed performance is shown in the following table:
1. Technical performance of the one-component potting material prepared with 2-3 % PM2100 accelerator (curing agent : accelerator = 5 : 1):
Curing conditions |
Curing shrinkage |
Volume resistivity |
Breakdown voltage |
Dielectric constant |
Tangent of the dielectric loss angle |
Shelf life |
130 °C 30 min 150 °C 20 min |
1 % |
5×1,015 Ω cm |
28 kv / mm |
3.8 |
3×10-2 |
> 6 months |
2. Comparison of the Performance of vehicle folding adhesives prepared with PM2100 accelerator and other accelerators:
Accelerator |
Tertiary amine salt |
Imidazole salt |
A100 accelerator |
Phenate |
Amine salt |
Gelation time T (160 ℃) |
1 min 50 sec |
1 min 4 sec |
2 min 35 sec |
8 min without gelation |
8 min without gelation |
Shear strength (Mpa) 160 ℃ 30 min |
27 |
23.6 |
28 |
|
|
Remarks: PM2100 has higher activity, better storage conditions, and can meet more stringent environmental protection requirements than others.